ARMOPUR® DTM 113 SEMIGLOSS
Primer‑finish coating two‑component semi‑gloss acrylic‑polyurethane anticorrosive, weather‑resistant. An aliphatic polyisocyanate is used as the hardener.
Gloss - 36‑60% depending on the color;
Покрытие
thick‑coat application
Химическая основа
acrylic‑polyurethane
Цвет
Colored according to RAL, NCS and sample
Тип поверхности
steel
galvanized steel
aluminum
plastics (except PP and PE)
2K primers
Степень блеска
semi‑gloss
- When applied in two layers, it can be used as a standalone coating;
- Zinc phosphate is used as the anticorrosive pigment;
- Excellent resistance to atmospheric exposure and wear;
- Suitable for use as a semi‑gloss topcoat for epoxy and acrylic‑polyurethane systems exposed to atmospheric and/or chemical conditions;
- Recommended for painting transport vehicles, equipment, external surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Solid content of the mixture: 56 ± 2 % | *60 ± 2 %.
- Solid content of the base: 55–75 %.
- Mixture density: 1.1–1.2 kg/L.
- Base viscosity: >180 s (DIN4).
- Mixture viscosity: 65–85 s (DIN4).
- Mixture pot life: 4 h.
- Drying time for a 50 µm dry film thickness:
- +10 °C:
- Dry to dust: 30 min
- Recoat: 6 h
- Minimum intercoat drying: 15 min
- +23 °C:
- Dry to dust: 20 min
- Recoat: 4 h
- Minimum intercoat drying: 5–7 min
- +35 °C:
- Dry to dust: 10 min
- Recoat: 2 h
- Minimum intercoat drying: 5 min
- Temperature drying:
- +60 °C: 30 min
Complete film formation: 7 days under ambient drying.
Data are given at 65 % relative humidity. Values may change with humidity variation.
* Version with ARMOPUR Hardener 61 | 63