ARMOPUR® TOPCOAT 111 "GRAPHITE"
Two‑component acrylic‑polyurethane weather‑resistant enamel with a decorative effect. Contains MIOX – iron silicate. Produces a rough metallic effect resembling fine‑grit sandpaper, with iridescent highlights and relief, accentuating the shape of forged and decorative elements. An aliphatic isocyanate is used as the curing agent.
Покрытие
special effect for forging
Химическая основа
acrylic‑polyurethane
Цвет
Special effects
Тип поверхности
2K primers
Степень блеска
special decorative effect
- Applied to a primed surface;
- Forms an atmospheric-resistant coating capable of retaining color and gloss over a long service period;
- Suitable for use as a glossy topcoat in systems with epoxy and acrylic-polyurethane primers;
- Recommended for painting transport, equipment, exterior surfaces of tanks, steel frames and other steel structures, and machine equipment.
- Solid content of the mixture: 51 ± 2%.
- Solid content of the base: 65–85%.
- Mixture density: 1.5–1.6 kg/L.
- Base viscosity: >180 s (DIN4).
- Mixture viscosity: 50–70 s (DIN4).
- Mixture pot life: 4 h.
- Drying time for a dry film thickness of 50 µm:
- +10 °C:
- Dust free: 30 minutes
- Touch dry: 6 hours
- Minimum intercoat drying: 15 minutes
- +23 °C:
- Dust free: 20 minutes
- Touch dry: 4 hours
- Minimum intercoat drying: 5–7 minutes
- +35 °C:
- Dust free: 10 minutes
- Touch dry: 2 hours
- Minimum intercoat drying: 5 minutes
- Thermal drying:
- +60 °C: 30 minutes
Full coating cure: 7 days under ambient drying.
Data are given at 65 % relative humidity. Values may change with humidity variation.