ARMOPUR® DTM 113 FD
Two-component fast-drying acrylic-polyurethane coating. Contains zinc phosphate. Used as a topcoat or as a standalone coating for direct application to metal. Forms a semi-matte, durable coating with good color retention. Application is permitted at temperatures down to −10 °C. Easily applied by airless spraying.
Specific Feature
fast drying
Product Chemistry
acrylic-polyurethane
Color Options
tinted according to RAL, NCS and sample
Surface Type
steel
galvanized steel
aluminum
plastics (except PP and PE)
2K primers
Gloss Level
semi-matte
- Anticorrosion protection and repair of metal and concrete structures in civil construction, the petrochemical complex, transport construction and heavy engineering, operated in various corrosive environments:
C2–C5, CX (GOST 34667.5—2021)
KhA1–KhA3 (SN 2.01.07-2020)
- Volume solids of the mixture: 62 ± 2%.
- Mixture density: 1.29 kg/L.
- Mixture viscosity: thixotropic.
- Pot life of the mixture: at least 2 hours at +20 °C.
- Drying time to degree 3 according to GOST 19007:
- +20 °C: no more than 1 hour.
- Minimum intercoat drying: 2 hours at +20 °C.
- Recommended dry film thickness: 60–120 µm.
- Theoretical consumption: 125 g/m² at a dry film thickness of 60 µm (excluding losses).
- Adhesion:
- Cross-cut method: no more than 1 point.
- Pull-off method: at least 4 MPa.
- Application temperature: from −10 °C.
- Material temperature: not below +15 °C.
- Maximum relative air humidity: 85%.
- Gloss level: 20–40 GU (semi-matte surface).
- Mixing ratio by weight: 100 : 12.5 (base : Hardener 61).
- Mixing ratio by volume: 100 : 20 (base : Hardener 61).
- Thinner: Thinner 3.
- Airless spraying: up to 10% by weight.
- Air spraying: up to 20% by weight.
- Brush/roller: up to 10% by weight.
- Shelf life: 24 months in unopened factory packaging.
Drying time data are given at +20 °C. Drying time at other temperatures is not specified in the technical data sheet.